Strip Baja Tahan Karat 321
Pasokan Baogu Kelas Pelat Baja Tahan Karat
| Jenis | Nilai | Nilai | Komponen Kimia % | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Lainnya | |||
| Austenitik | 201 | SUS201 | ≤0,15 | 16.00-18.00 | 3.50-5.50 | 5.50－7.50 | ≤0,060 | ≤0,030 | - | ≤1.00 | - | ≤0,25 | - |
| 202 | SUS202 | ≤0,15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ≤0,060 | ≤0,030 | ≤1.00 | - | ≤0,25 | － | ||
| 301 | 1.431 | ≤0,15 | 16.00-18.00 | 6.00-8.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | ≤0,10 | - | |
| 304 | 1.4301 | ≤0,07 | 17.00-19.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 304L | 1.4307 | ≤0,030 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 304 jam | 1.4948 | 0,04-0,10 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 309 | 1.4828 | ≤0,20 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 309S | * | ≤0,08 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 310 | 1.4842 | ≤0,25 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 310S | * | ≤0,08 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 314 | 1.4841 | ≤0,25 | 23.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | 1,50-3,00 | - | - | - | |
| 316 | 1.4401 | ≤0,08 | 16.00-18.50 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316L | 1.4404 | ≤0,030 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316Ti | 1.4571 | ≤0,08 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1.00 | - | 0,1 | Ti5(C+N)~0,70 | |
| 317 | * | ≤0,08 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1.00 | - | 0,1 | - | |
| 317L | 1.4438 | ≤0,03 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1.00 | - | 0,1 | - | |
| 321 | 1.4541 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Ti5(C+N)~0,70 | |
| 321 jam | * | 0,04-0,10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Ti5(C+N)~0,70 | |
| 347 | 1.455 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Nb≥10*C%-1,10 | |
| 347 jam | 1.494 | 0,04-0,10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Nb≥10*C%-1,10 | |
| xm-19 | Nitronik50 | ≤0,06 | 20.50-23.50 | 11.50-13.50 | 4.0-6.0 | ≤0,045 | ≤0,030 | 1,50-3,00 | ≤1.00 | - | 0,2-0,4 | NB :0.10-0.30 V :0.10-0.30 | |
| 904L | N08904 | ≤0,02 | 19.0-23.0 | 23.0-28.0 | 4.0-5.0 | ≤0,045 | ≤0,035 | ≤1.00 | 0,1 | Cu:1.0-2.0 | |||
| Rangkap | 2205 | S32205 | ≤0,03 | 22.0-23.0 | 4.5-6.5 | ≤2.00 | ≤0,030 | ≤0,020 | 3.0-3.5 | ≤1.00 | - | 0,14-0,20 | |
| 2507 | S32750 | ≤0,03 | 24.0-26.0 | 6.0-8.0 | ≤1.20 | ≤0,035 | ≤0,020 | 3.0-5.0 | ≤0,80 | 0,5 | 0,24-0,32 | ||
| * | S32760 | ≤0,03 | 24.0-26.0 | 6.0-8.0 | ≤1.00 | ≤0,030 | ≤0,010 | 3.0-4.0 | ≤1.00 | 0,5-1,00 | 0,2-0,3 | ||
| 2304 | S32304 | ≤0,03 | 21.5-24.5 | 3.0-5.5 | ≤2,50 | ≤0,040 | ≤0,030 | 0,05-0,6 | ≤1.00 | 0,05-0,6 | 0,05-0,2 | ||
| 329 | 1.446 | ≤0,08 | 23.00-28.00 | 2.00-5.00 | ≤1.00 | ≤0,040 | ≤0,030 | 1.00-2.00 | ≤0,75 | - | - | ||
| Ferit | 409 | S40900 | ≤0,03 | 10.50-11.70 | 0,5 | ≤1.00 | ≤0,040 | ≤0,020 | - | ≤1.00 | - | ≤0,030 | Ti6(C+N)~0,50 Nb:0,17 |
| 430 | 1Cr17 | ≤0,12 | 16.00-18.00 | - | ≤1.0 | ≤0,040 | ≤0,030 | - | ≤1.0 | - | - | - | |
| 444 | S44400 | ≤0,025 | 17.50-19.50 | 1 | ≤1.00 | ≤0,040 | ≤0,030 | 1.75-2.5 | ≤1.00 | - | 0,035 | Ti+Nb:0,2+4(C+N)~0,80 | |
| 446 | S44600 | ≤0,20 | 23.00-27.00 | 0,75 | ≤1.5 | ≤0,040 | ≤0,030 | 1,50-2,50 | ≤1.00 | - | ≤0,25 | - | |
| Martensit | 410 | 1Cr13 | 0,08-0,15 | 11.50-13.50 | 0,75 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - |
| 410S | * | ≤0,080 | 11.50-13.50 | 0,6 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 416 | Y1Cr13 | ≤0,15 | 12.00-14.00 | 3) | ≤1.25 | ≤0,060 | ≥0,15 | - | ≤1.00 | - | - | - | |
| 420 | 2Cr13 | ≥0,15 | 12.00-14.00 | - | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 420J2 | 3Cr13 | 0,26-0,35 | 12.00-14.00 | - | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 431 | 1Cr17Ni2 | ≤0,20 | 15.00-17.00 | 1,50-2,50 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤0,80 | - | - | - | |
| 440C | 11Cr17 | 0,95-1,20 | 16.00-18.00 | - | ≤1.00 | ≤0,040 | ≤0,030 | 0,75 | ≤1.00 | - | - | - | |
| PH | 630 | 17-4PH | ≤0,07 | 15.00-17.50 | 3.00-5.00 | ≤1.00 | ≤0,035 | ≤0,030 | - | ≤1.00 | 3.00-5.00 | - | Catatan 0,15-0,45 |
| 631 | 17-7PH | ≤0,09 | 16.00-18.00 | 6.50-7.50 | ≤1.00 | ≤0,035 | ≤0,030 | - | ≤1.00 | ≤0,50 | - | Al 0,75-1,50 | |
| 632 | 15-5PH | ≤0,09 | 14.00-16.00 | 3.50-5.50 | ≤1.00 | ≤0,040 | ≤0,030 | 2.00-3.00 | ≤1.00 | 2.5-4.5 | - | Al 0,75-1,50 | |
Keterangan
Strip baja tahan karat 321 merupakan jenis baja tahan karat austenitik dengan kandungan karbon rendah dan ketahanan korosi yang baik terhadap banyak lingkungan korosif.321 menawarkan kemampuan las yang sangat baik, kemampuan mesin yang baik, dan sifat fabrikasi yang luar biasa.
Strip baja tahan karat 321 biasa digunakan pada industri kimia, industri pulp dan kertas, industri teknik kelautan dan lepas pantai serta pada industri makanan dan minuman.
Strip baja tahan karat 321 juga memiliki tingkat ketahanan yang tinggi terhadap retak dan lubang korosi tegangan klorida.Ia juga tahan terhadap asam klorida pada suhu tinggi hingga 250°C (480°F).
Fitur
Ketahanan Korosi yang Baik: Strip baja tahan karat 321 memiliki ketahanan korosi yang lebih baik daripada baja tahan karat jenis 304 dan 316, sehingga ideal untuk digunakan di lingkungan korosif.
Kemampuan Las yang Sangat Baik: Strip baja tahan karat 321 dapat dilas dengan semua metode termasuk pengelasan busur (TIG / GTAW), pengelasan berkas elektron (EBW / EFW), pengelasan busur terendam (SAW) dan pengelasan sinar laser (LBIW).
Kekuatan Tinggi: Tingkat kekuatan strip baja tahan karat 321 hingga 50% lebih tinggi dibandingkan dengan baja tahan karat jenis 304 dan hingga 80% lebih tinggi dibandingkan dengan baja tahan karat jenis 316 karena peningkatan kandungan karbon dan ukuran butir austenitnya.